Produse pentru 2 epoxid componentă (9)

EG 91 Epoxy-polyurethane two-component elastoplastic and thixotropic sealant, for joints subject to traffic, where Shore A Hardness Scale = 65. The elongation-at-break is 70%. To be applied with a trowel or extruded into the suitably-taped sections of the joint (to protect adjacent surfaces). Resistant to contact with hydrocarbons (gasoline and diesel fuel). Horizontal sealing of joints in industrial flooring, even in the presence of chemical attacks and stresses from average-heavy traffic. Vertical sealing of joints in concrete works and products. The application and containment surfaces (joint walls) should be clean, dry, conveniently prepared and adequately resistant: free from dust, grease, soiling, crumbling and/or non-adhering parts and dry. The application surfaces must also be preliminarily treated with Protech Flex Primer. Add component B to component A taking care to pick up all the material contained in the packs, mix thoroughly with a mixer at a low number of revolutions, until a perfectly homogeneous mix is obtained; add the required load amount (component C) continue to mix until a perfectly homogeneous mixture is obtained, indicated by the uniform colour of the mixture. Apply the product mixed by trowelling or with extrusion guns. Do not apply with temperatures below + 5°C or higher than + 35°C and in the presence of surface stagnant water. Approximately 1.25 kg of EG 91 per cubic decimetre of joint volume to be sealed (1250 kg per cubic metre). Packaging: Kit of 5+2.5 kg UM: €/kg

Thermische Spritzverfahren Lichtbogenspritzen Atmosphärisches Plasmaspritzen Pulverflammspritzen Drahtflammspritzen Hochgeschwindigkeits-Flammspritzen (HVOF) Nachbehandlung von Spritzschichten Versiegeln Ofensintern Drehen/Schleifen/Läppen/Honen Qualitätssicherung von Spritzschichten Prüfen und Messen der Bauteile Prüfen auf Rissfreiheit Messen der Oberflächenhärte Messen der Oberflächenrauheit Erstellen eines metallographischen Schliffes

Système époxy transparent. Dureté variable. Facile d'emploi. -> Application Décoration, décoration florale, imitation de liquide, simulation de cours d'eau en maquettes. Couleur : Transparent Ratio mélange : 100/100 Potlife : 70 min à 9h Temps avant démoulage : >48h TG°C : nc Unité de vente : 1 kit de 2kg Minimum de commande : 1 kit

Film de protection de couleur permettant de changer la couleur d'un véhicule tout en aillant la protection du film PPF (auto cicatrisation, brillance, protection UV, protection film routier...

Syntech Pavidamp A three-component formulation, with a fluid epoxy resin base in aqueous emulsion (A + B) to be mixed with the third component (C) consisting of white cement and micro-quartz, specially designed to be used as a primer for cementitious surfaces in the presence of humidity and in conditions of hydraulic counter-thrust. Generally referred to as “wet-bonding”, it is particularly suitable as an anti-humidity barrier for the subsequent laying of parquet. Building connection layers and smoothing cement surfaces; bottom layers for resinous coatings of floorings in the presence of damp subbases; anti-humidity barriers in concrete, brick and stone masonry; surfacings of porosity, cracks and superficial irregularities. As protection from rising damp for bases where operations with polyurea resins SYNTECH POLYUREA will be carried out. The support on which the resin system is to be laid must be suitable for withstanding the stresses resulting from the intended use, such as static or dynamic loads, impacts, thermo-hygrometric dilatations, vibrations, etc. As regards the characteristics of the substrate (maximum humidity, cohesion, strength class, flatness, etc.) and the preparation of the surface that will accommodate the resin system, we recommend the requirements set out in chapter 5 of the UNI 10966 standard ("RESIN SYSTEMS FOR SURFACES HORIZONTAL AND VERTICAL - INSTRUCTIONS FOR DESIGN AND APPLICATION "). In any case, carefully clean and degrease the surfaces, removing any kind of dirt, paint residues or incoherent parts. Evaluate the most convenient type of mechanical preparation (shot peening, sandblasting, hydro-washing, etc.). The surfaces must also be free from discontinuity, and possibly leveled and regularized with products from the FLOOR line or the REPAR line. Apply by roller, brush or spray from 150 to 200 g / m2 of Syntech Primer EP-W to consolidate the substrate and facilitate the adhesion of the subsequent coating. Tiled floors, or floors covered with pre-existing resin, must be subjected to mechanical roughening carried out with shot blasting, milling, bush hammering, etc., until the total elimination of the waterproof crust and the opacification of the surfaces. Remove dust after abrasion. Prepare the mixture of the 2 liquid components (A+B), pouring the contents of the component B in the container of the component A. Mix with drill for about 2 minutes. Add the pre-dosed hydraulic binder (high resistance white cement) to the mixture A+B, and mix with a mixer drill. To disperse the product optimally, pour the powders (component C) a little at a time, continuing to stir with drill, until a homogeneous lump-free mixture is obtained. If it is used as a base: dilute with 10-15% by weight of clean, soft water and apply with a roller or brush. Indicative consumption: 0.4-0.5 kg/m² on regular supports, 0.7-0.9 kg/m² on irregular supports. If it is used for fine finishing coats: load the system A+B+C diluted with 10-15% of fresh clean water, with 60-70% spheroidal quartz (0.04-0.25 mm). Apply with steel trowel or plastering trowel. Indicative consumption: 1-2 kg/m². If it is used for medium finishing coats: load the system A+B+C diluted with 10-15% of fresh clean water, with 70-80% spheroidal quartz (0.1-0.5 mm). Apply with steel trowel or plastering trowel. Indicative consumption: 3-4 kg/m². From 0.50 to 0.60 kg of SYNTYECH PAVIDAMP for each square metre of surface to be covered. Pail 3.8 kg [A] - Pail 1.2 kg [B] - Pail 5 kg [C] - Kit: 1 Pail 3.8 kg [A] + 1 Pail 1.2 kg [B] + 1 Pail 5 kg [C]

Syntech Poliurea Primer – Epoxy Metal Syntech Poliurea Primer – Epoxy Metal is a two-component primer based on epoxy resins free from solvents, used to promote adhesion, as a surface sealant for concrete, applied as a substrate for works with polyureas on metal surfaces and epoxy and polyurethane coatings. Adhesion promoter, surface sealant for concrete, to be applied as a substrate for works with polyureas on metal surfaces and epoxy and polyurethane coatings. The application must take place on a dry and degreased surface; the substrate must not have crumbly or detached parts and with a degree of humidity that must not exceed 5%. Preparation of the substrate may require some types of mechanical action: Smoothing, bush-hammering, shot peening, hydro-washing. Other mechanical actions that can make the support suitable. The individual components must be mixed carefully until a homogeneous mass is obtained. The material can be applied by roller, brush or spray by means of special airless machines, even in two coats. The temperature of the support must always be at least 3°C higher than the dew point temperature. Minimum application temperature +5°C, maximum temperature +35°C. Approximately 0,20 kg of Syntech Poliurea Primer – Epoxy Metal for every square metre of surface to be treated. Can 10 kg [A] - Can 5 kg [B] - Kit: 1 Can 10 kg [A] + 1 Can 5 kg [B]

Syntech Poliurea Top Coating A protective, pigmented, two-component formulation based on aliphatic polyurethane resins, ideal as a protective and aesthetic coating on waterproofing with SYNTECH POLIUREA SPRAY. Characterised by high levels of elasticity and elevated protection, even in aggressive atmospheres. Available on request in shades from the RAL colour range. Surface coating pigmented for colouring polyurethane claddings, and their protection from UV rays (which in the absence of the top coating would alter the colour over time). After suitable priming with SYNTECH POLYUREA PRIMER, it can also be applied as a simple coloured aliphatic protective coating. Polyurea support Vacuum and blow the surfaces to eliminate any dust that may have accumulated in the 24-48 hours following the installation of SYNTECH POLIUREA SPRAY Support in concrete, mortar, brick, tiles The support on which the polyurea system must be laid must be suitable for withstanding the stresses resulting from the intended use, such as static or dynamic loads, impacts, thermo-hygrometric dilations, vibrations, etc. As regards the characteristics of the substrate (maximum humidity, cohesion, strength class, flatness, etc.) and the preparation of the surface that will accommodate the resin system, we recommend the requirements set out in chapter 5 of the UNI 10966 standard ("RESIN SYSTEMS FOR SURFACES HORIZONTAL AND VERTICAL - INSTRUCTIONS FOR DESIGN AND APPLICATION "). In any case, carefully clean and degrease the surfaces, removing any kind of dirt, paint residues or incoherent parts. The humidity of the support must be <= 3%. Evaluate the most convenient type of mechanical preparation (shot peening, sandblasting, hydro-washing, etc.). The surfaces must also be free from discontinuity, and possibly leveled and regularized with products from the FLOOR line or the REPAR line. In case of presence (even suspected) of humidity deriving from capillary rising from the substrate, it is recommended to apply in advance the epoxy resin for "wet substrates" Syntech Pavidamp. Tiled floors, or floors covered with pre-existing resin, must be subjected to mechanical roughening carried out with shot blasting, milling, bush hammering, etc., until the total elimination of the waterproof crust and the opacification of the surfaces. Remove dust after abrasion. It is recommended to use Primer from the SYNTECH POLIUREA PRIMER range. On particularly absorbent substrates, to avoid the formation of craters / blowholes on the surface of the freshly sprayed product, it is recommended to use primers from the SYNTECH POLIUREA PRIMER range, always contacting the Azichem technical staff for clarification on the most suitable type to use. Apply several layers of primer until the porosity is saturated and providing a light dusting with clean and dry quartz sand (0.4-0.7 mm). Never dust off the primer. Provide suitable elastic sealing systems to cover joints, fittings, cracks or fissures subject to significant movements. Pour component B with component A into a single container, taking care to remove all the material from the packaging. Mix thoroughly with a mixer at low revs, until a lump-free mixture is obtained. Apply with a roller or brush on the surfaces of SYNTECH POLYUREA SPRAY, within 24-48 hours of spreading the latter. A thorough sanding of the supports is recommended for any repairs and/or finishes. From 0.15 to 0.25 kg of SYNTYECH POLIUREA TOP COATING for each square metre of surface to be covered. Can 6.7 kg [A] - Can 3.3 kg [B] - Kit: 1 Can 6.7 kg [A] + 1 Can 3.3 kg [B]

REFERENCE : ARTP3200TCR25 ALPHA 3200 coloré PLATRE 3200 T.CUITE ROUGE 25kg -> Descritpion PLATRE DE MOULAGE COLORE POUR L'INDUSTRIE STATUAIRE -> Domaine d'application Produit teinté, spécialement conçu pour l'industrie statuaire : - Moulages durs, - Maquettes, - Statuettes, et ornement. -> Caractéristique Unité de vente : bidon de 25kg Minimum de vente : un bidon

REFERENCE : RESMPP16095 (ex PP1609)36kg/m2. RESIFOAM BAYMER AL759 5kg...kg MOUSSE POLYURETHANE RESIFOAM. Mousse polyuréthane expansive rigide approprié pour le remplissage d'élements par coulée. Applications:isolation industrielle,remplissage, reserves de flotabilité etc... MELANGE: 100parts RESIFOAM + 100parts DESMODUR(en volume)